European standard EN 10346/09 |
Automotive Industry Association VDA 239-100 |
---|---|
HX180YD + Z, | CR180IF-GI |
HX220YD + Z, | CR210IF-GI |
HX260YD + Z | |
HX300YD + Z, | |
HX220PD + Z, + ZF 1) | |
HX260PD + Z, |
Grades according to EN 10346/09 |
CMAX | MnMAX | PMAX | SMAX | SiMAX | Al | TiMAX | NbMAX |
---|---|---|---|---|---|---|---|---|
HX180YD + Z, | 0,01 | 0,70 | 0,06 | 0,025 | 0,20 | min. 0,1 | 0,12 | 0,09 |
HX220YD + Z, | 0,01 | 0,90 | 0,08 | 0,025 | 0,20 | min. 0,1 | 0,12 | 0,09 |
HX260YD + Z, | 0,01 | 1,30 | 0,10 | 0,025 | 0,25 | min. 0,1 | 0,12 | 0,09 |
HX300YD + Z, | 0,015 | 1,6 | 0,1 | 0,025 | 0,3 | min. 0,1 | 0,12 | 0,09 |
HX220PD + Z, + ZF 1) | 0,06 | 0,70 | 0,08 | 0,025 | 0,50 | min. 0,02 | - | - |
HX260PD + Z, | 0,11 | 0,70 | 0,10 | 0,025 | 0,50 | min. 0,02 | - | - |
1) according to EN 10292/2000 + A2/04
Grades according to EN 10346/09 |
Rp0,2 [MPa] |
Rm [MPa] |
A MIN (%) Lo = 80 mm |
r90 min. |
n90 min. |
---|---|---|---|---|---|
HX180YD + Z, | 180 - 240 | 330 -390 | 34 | 1,7 | 0,18 |
HX220YD + Z, | 220 - 280 | 340 - 420 | 32 | 1,5 | 0,17 |
HX260YD + Z, | 260 - 320 | 380 - 440 | 30 | 1,4 | 0,16 |
HX300YD + Z, | 300 - 360 | 390 - 470 | 27 | 1,3 | 0,15 |
HX220PD + Z, ZF | 220 - 280 | 340 - 400 | 32 | 1,3 | 0,15 |
HX260PD + Z, | 260 - 320 | 380 - 440 | 28 | - | - |
Nominal thickness | 800 | 1100 | 1300 | 1380 | 1500 | |
---|---|---|---|---|---|---|
0,50 - 0,59 | ||||||
0,60 - 0,89 | ||||||
0,90 - 1,49 | ||||||
1,50 - 2,00 |
Nominal thickness | Sheet length | Coil diameter | Slit coil width | Nominal coil weight [kg.mm -1 of width] |
|
---|---|---|---|---|---|
inner | outer | ||||
0,45 - 2,00 | 1 000 - 3 100 | approx. 500 | max. 1 400 | 40 - 600 (depending on sheet thickness) |
3 - 9,9 |
approx. 600 | |||||
2 - 9,4 |
Thickness is graded by 0,01 mm, width is graded by 5,0 mm, length is graded by 5 mm; nominal thickness includes zinc coat.
Nominal thickness | Normal tolerances at width | Reduced tolerances at width | ||
---|---|---|---|---|
≤ 1 200 | >1 200 ≤ 1 500 | ≤ 1 200 | >1 200 ≤ 1 500 | |
> 0,40 ≤ 0,60 | ± 0,04 | ± 0,05 | ± 0,035 | ± 0,040 |
> 0,60 ≤ 0,80 | ± 0,05 | ± 0,06 | ± 0,040 | ± 0,045 |
> 0,80 ≤ 1,00 | ± 0,06 | ± 0,07 | ± 0,045 | ± 0,050 |
> 1,00 ≤ 1,20 | ± 0,07 | ± 0,08 | ± 0,050 | ± 0,060 |
> 1,20 ≤ 1,60 | ± 0,10 | ± 0,11 | ± 0,060 | ± 0,070 |
> 1,60 ≤ 2,00 | ± 0,12 | ± 0,13 | ± 0,070 | ± 0,080 |
NOTE: reduced tolerances are the subject to prior agreement
Nominal width | Normal tolerances at thickness | Reduced tolerances at thickness | |||
---|---|---|---|---|---|
< 0,70 | ≥ 0,70 < 2,00 | < 0,70 | ≥ 0,70 < 1,60 | ≥ 1,60 ≤ 2,00 | |
≥ 600 < 1 200 | 10 | 8 | 5 | 4 | 3 |
≥ 1 200 < 1 500 | 12 | 10 | 6 | 5 | 4 |
≥ 1 500 | 17 | 15 | 8 | 7 | 6 |
NOTE: flatness tolerances valid only for plates
Nominal thickness | 800 | 1150 | 1250 | 1300 | 1350 | 1380 | 1500 | |
---|---|---|---|---|---|---|---|---|
0,50 - 0,59 | ||||||||
0,60- 0,79 | ||||||||
0,80 - 0,89 | ||||||||
0,90 - 1,09 | ||||||||
1,10 - 1,69 | ||||||||
1,70 - 2,00 |
Nominal thickness | Sheet length | Coil diameter | Slit coil width | Nominal coil weight [kg.mm -1 of width] |
|
---|---|---|---|---|---|
inner | outer | ||||
0,50 - 2,00 | 1 000 - 3 100 | cca 500 | max. 1 400 | 40 - 600 (v závislosti na hrúbke plechu) |
3 - 9,9 |
cca 600 | |||||
2 - 9,4 |
Thickness is graded by 0,01 mm, width is graded by 5,0 mm, length is graded by 5 mm; nominal thickness includes zinc coat
Nominal thickness | 800 | 1000 | 1100 | 1300 | 1350 | 1380 | 1500 | |
---|---|---|---|---|---|---|---|---|
0,50 - 0,59 | ||||||||
0,60- 0,79 | ||||||||
0,80 - 0,99 | ||||||||
1,00 - 1,09 | ||||||||
1,10 - 1,69 | ||||||||
1,70 - 2,00 |
Nominal thickness | Sheet length | Coil diameter | Slit coil width | Nominal coil weight [kg.mm -1 of width] |
|
---|---|---|---|---|---|
inner | outer | ||||
0,50 - 2,00 | 1 000 - 3 100 | cca 500 | max. 1 400 | 40 - 600 (v závislosti na hrúbke plechu) |
3 - 9,9 |
cca 600 | |||||
2 - 9,4 |
Thickness is graded by 0,01 mm, width is graded by 5,0 mm, length is graded by 5 mm; nominal thickness includes zinc coat
Nominal thickness |
Normal tolerances at width | Reduced tolerances at width | ||
---|---|---|---|---|
≤ 1 200 | >1 200 ≤ 1 500 | ≤ 1 200 | >1 200 ≤ 1 500 | |
> 0,40 ≤ 0,60 | ± 0,05 | ± 0,06 | ± 0,040 | ± 0,045 |
> 0,60 ≤ 0,80 | ± 0,06 | ± 0,07 | ± 0,045 | ± 0,050 |
> 0,80 ≤ 1,00 | ± 0,07 | ± 0,08 | ± 0,050 | ± 0,060 |
> 1,00 ≤ 1,20 | ± 0,08 | ± 0,09 | ± 0,060 | ± 0,070 |
> 1,20 ≤ 1,60 | ± 0,11 | ± 0,13 | ± 0,070 | ± 0,080 |
> 1,60 ≤ 2,00 | ± 0,14 | ± 0,15 | ± 0,080 | ± 0,090 |
NOTE: reduced tolerances are the subject to prior agreement
Nominal width | Normal tolerances at thickness | Reduced tolerances at thickness | |||
---|---|---|---|---|---|
< 0,70 | ≥ 0,70 < 2,00 | < 0,70 | ≥ 0,70 < 1,60 | ≥ 1,60 ≤ 2,00 | |
≥ 600 < 1 200 | 13 | 10 | 8 | 6 | 5 |
≥ 1 200 < 1 500 | 15 | 13 | 9 | 8 | 6 |
≥ 1 500 | 20 | 19 | 12 | 10 | 9 |
NOTE: flatness tolerances valid only for plates
Zinc coating (Z) |
Min. weight of surface coating from both sides [g.m-2] |
---|---|
same | 100; 140; 150; 180; 200; 225; 275;(350) |
differential | 140/100; 150/85; |
Zinc-iron coating (ZF) |
Min. weight of surface coating from both sides [g.m-2] |
---|---|
same | 90; 100; 110; 120 |
Other dimensions are subject to prior agreement
Informative thickness of zinc layer: 7g.m-2 ≈ 1μm